Rostfritt stål, Höglegerat stål

Extra low-carbon stainless steel electrode of type 18Cr 12Ni 2.8Mo intended for position welding mainly of thin-walled pipes. The electrode has a thin casing and can be welded according to the so-called ''drop welding method'' or vertical falling, which is faster. This requires an electrode with very good ignition and re-ignition properties, which makes OK 63.20 very suitable. The electrode is directly adapted for the stainless steels of types 316 and 316L, for example X3CrNiMo17-13-3 (SS2343), X2CrNiMo18-14-3 (SS2353) or corresponding steel according to other standards. The weld metal's low carbon content provides good resistance to intercrystalline corrosion but also to pitting and most types of corrosion in reducing and neutral solutions. OK 63.20 can also be used for welding stabilized steels if these are not to be operated at temperatures above 400°C. /B>
DC+, AC, open-circuit voltage (OCV) 50 V
Examples of corresponding additive materials:
TIG: OK Tigrod 16.32
MAG: OK Autrod 16.32
Tubing wire: OK Tubrod 14.21
Electrode class:
EN 1600: E 19 12 3 L R 1 1
SFA/AWS A5.4: E316L-16
Werkstoff Nr: 1.4430
CSA W48: E316L-16
Typical values ??of all-weld material:
Chemical composition %:
C: <0.03, Si : 0.50-1.00 Mn: 0.5-1.2, Cr: 17.5-19.0, Ni: 11.0-13.0, Mo: 2.5-3.0
Mechanical values:
Yield limit (Rp0 ,2): 480 MPa
Breaking strength (Rm): 590 MPa
Elongation (A5): 41%
Impact toughness, KV:
Test temperature/Impact toughness value: +20° C/56 J, -60°C/46 J
Ferrite number: FN 3-10
Approvals:
CWB: CSA W48, Seproz: UNA 272580, VdTÜV: 09716, CE: EN 13479

Typ Rutil-sur. Extra lågkolhaltig, lättsvetsad, rostfri syrafast elektrod av typ 18,5% Cr, 12,5% Ni och 2,8% Mo. Ger vackra kälsvetsar. Ferrithalt FN ca 8. LMA-effekt. Ström Amp. DC+, AC OCV 50 V.

(HTML text not available)

Overalloyed stainless electrode for welding stainless to other types of steel. However, OK 92.26 should be used for welding stainless against heat-resistant steels, for example SS 2116, SS 2218 (10CrMo9-10) at high operating temperatures. The electrode is suitable for bottom strings in the transition between the unalloyed and stainless layers of compound plates. OK 67.70 has excellent welding properties on both direct and alternating current. It can be used in all positions except vertically downwards and in all existing joint types. For horizontal welding in thicker materials, the fast-welding high-yield electrode OK 67.71 can be a good alternative to OK 67.70.
Return:
120%
Type of current:
DC+, AC, open circuit voltage (OCV) 55 V
Example of corresponding additive material:
TIG: OK Tigrod 16.54
MAG: OK Autrod 16.54
Tube wire: OK Tubrod 14.33 , 15.32
Electrode class:
EN 1600: E 23 12 2 L R 3 2
SFA/AWS A5.4: E309MoL-17
Werkstoff Nr: 1.4459
CSA W48: E309MoL-17
Typical values ??of all-weld material:
Chemical composition %:
C: 0.03C, Si: 0.8, Mn: 0.8, Cr: 23.0, Ni: 13.0, Mo: 2.7
Mechanical values:
Strength (Rp0.2): 510 MPa
Breaking strength (Rm): 610 MPa
Elongation (A5): 32%
Impact toughness, KV:
Test temperature/Impact toughness value: +20°C/50 J
Ferrite number : FN 12-22
Approvals:
ABS: SS to C&C/Mn steels, CWB: CSA W48, DB: 30.039.05, DNV: 309 Mo, LR: SS /CMn, RINA: E 309Mo, Sepros: UNA 409820, VdTÜV: 02424, CL: EN 1600, BV: UP, CE: EN 13479

Extra low-carbon stainless steel wire electrode for gas metal arc welding of austenitic stainless steels containing approx. 19 Cr, 10 Ni. OK Autrod 380LSi is recommended for eg AISI 304, 404 L and X5CrNi18-20 (SS2332, W.nr 1.4301) and SS2333, or equivalent stainless steels according to other standards. The increased content of silicon leads to better welding properties. For material thicknesses below 3 mm, short arc welding is easier to handle than spray arc welding. Bottom strands in chamfered joints are also most easily performed with short arc welding, while the remaining strands, at least in the case of horizontal welding, can be performed faster with spray arc welding.
Shield gas:
Ar+1-3%O2 (M13)
Type of current:
DC+
Example of corresponding additive material:
TIG: OK Tigrod 16.12
MMA: OK 61.30, 61.41
Conduit wire: OK Tubrod 14.20, 14.30, 15.30
SAW: OK Flux 10.92, 10.93 / OK Autrod 16.10
Electrode class:
SFA/AWS A5.9-93: ER308LSi
EN 12072: G 19 9 L Si
W.nr: 1.4316
Typical values ??of all-weld material:
Chemical composition %:
C: < ;0.03, Si: 0.8, Mn: 1.8, Cr: 20.3, Ni: 10.0
Mechanical values:
Yield limit (Rp0.2) :450 MPa
Breaking strength (Rm): 620 MPa
Elongation (A5): 36%
Impact toughness, KV:
Test temperature/Impact toughness value: +20°C/ 110 J, -60°C/90 J, -196(C/ 60 J
Ferrite number: FN 5-10
Approvals:
DB: 43.039.01, DnV: 308L MS (-60°C), Sepros: UNA 485178, UD: DIN 8556, VdTÜV: 04267, Ü: 43.039/1

Overalloyed extra low-carbon stainless steel wire electrode for gas metal arc welding of austenitic stainless steels (eg 316L and 308L) against ordinary unalloyed and low-alloyed steels. OK Autrod 309LSi is recommended for example for AISI 304, 404L and X5CrNi18-10 (SS2332, W. no.1.4301) and SS2333 or equivalent stainless steels according to other standards. It is also suitable for bottom strings in the transition between the stainless layer of the compound plate and the unalloyed one. The high silicon content results in good welding properties. For material thicknesses below 3 mm, short arc welding is easier to handle than spray arc welding. Bottom strands in chamfered joints are also most easily performed with short arc welding, while the remaining strands, at least in the case of horizontal welding, can be performed faster with spray arc welding.
Power type:
DC(+)
Example of corresponding additive material:
TIG: OK Tigrod 309LSi (16.51)
MMA: OK OK (67.70), 67.75
Tube wire: Shield-Bright 309L, Shield-Bright 309L X-tra
SAW: OK Flux 10.92, 10.93, OK Autrod 309L (16.53)
Electrode class:
SFA/AWS A5.9: ER309LSi
EN 12072: G 23 12 LSi
Werkstoffnummer: ~1.4332
Chemical composition %:
C: <0.02, Si: 0.8, Mn: 1.8, Cr: 24.0, Ni: 13 ,0,
Mechanical values:
Strength: 440 MPa
Breaking strength: 600 MPa
Elongation: 41%
Impact strength, KV:
Test temperature/Impact strength value:
+20°C/160J
-60°C/130J
-110°C/90J
Approvals:
CWB AWS: A5.9 (Article no. ending with A)
DB: 43.039.16
VdTÜV: 10020
CE: 13479

Extra low-carbon stainless steel wire electrode for gas metal arc welding of stainless steels containing approx. 18 Cr, 12 Ni, 3 Mo. Recommended for eg AISI 316, 316L. and 1.4436 (SS2343), 1.4435 (SS2353) or equivalent stainless steels according to other standards. The increased content of silicon leads to better welding properties. For material thicknesses below 3 mm, short arc welding is easier to handle than spray arc welding. Bottom strands in chamfered joints are also most easily performed with short arc welding, while the remaining strands, at least in the case of horizontal welding, can be performed faster with spray arc welding )
Shield gas:
Ar+1-3%O2 (M13)
Current type:
DC+
Example of corresponding additive material:
TIG: OK Tigrod 16.32
MMA: OK 63.20, 63.30, 63.34, 63.35, 63.41
Tube wire: OK Tubrod 14.21, 14.31, 15.31
SAW: OK Flux 10.92, 10.93 / OK Autrod 16.30
Electrode class:
EN 12072: G 19 12 3 L Si
SFA/AWS A5.9: ER316Lsi
W.nr: 1.4430
Typical values ??of all-weld material:
Chemical composition %:< BR>C: 0.02, Si: 0.8, Mn: 1.8, Cr: 18.5, Ni: 12.0, Mo: 2.7
Mechanical values:
Tensile strength (Rp0.2): 440 MPa
Break strength (Rm): 620 MPa
Elongation (A5): 37%
Impact strength, KV:
Test temperature /Impact resistance value: +20°C/ 120 J, -60°C/ 95 J, -196(C/55 J
Ferrite number: FN 5-10
Approvals:
DB: 43.039.05, DnV: 316L MS (-120°C), UDT: DIN 8556, VdTÜV: 04268, Ü: 43.039/1, CE: EN 13479, CWB: AWS A5.9 (item no ending with A)